Loctite LOCTITE 3D MED413 Resin White 1kg
LOCTITE MED413 is a medical-grade high-modulus photopolymer resin engineered for demanding healthcare applications. This tough yet flexible material combines exceptional mechanical properties with biocompatibility, making it perfect for medical devices like hearing aids that require both durability and precision.
- Medical grade certification with cytotoxicity and skin sensitization testing compliance.
- High modulus design provides excellent flexural and tensile strength for durable parts.
- Functions reliably at body temperature for medical device applications.
- Outstanding surface finish quality reduces post-processing requirements.
LOCTITE 3D MED413 RESIN
Medical Resins Designed for Durability
LOCTITE MED413 is a cutting-edge medical-grade high modulus photopolymer resin designed for exceptional flexural and tensile physical properties. Engineered with a unique blend of stiffness and toughness, this resin is perfect for crafting impact-resistant medical devices such as hearing aids. Available in clear and white, its benefits include the ability for parts to function seamlessly at body temperature, boasting an outstanding surface finish, and offering excellent machinability.
Key Features of the LOCTITE 3D MED413 Resin:
- Capable of meeting ISO 10993-5 & -10 standards for biocompatibility.
- Parts can function at body temperature.
- Compatible with a broad range of DLP machines.
- Excellent machinability for precise medical component manufacturing.
- Available in clear and white color options for versatile applications.
- Ideal for impact-resistant medical devices, including hearing aids.
- 50% elongation at break provides flexibility while maintaining strength.
Medical Grade Biocompatibility
MED413 meets stringent medical standards with full ISO 10993 compliance testing. The resin has passed cytotoxicity, irritation, and skin sensitization tests, ensuring safe contact with human tissue for medical device applications.
- ISO 10993-5 cytotoxicity certified.
- Skin sensitization tested per ISO 10993-10.
- Safe for body temperature operation up to 70°C.
Superior Mechanical Properties
This high modulus photopolymer delivers exceptional strength and toughness for demanding medical applications. The balanced combination of rigidity and flexibility makes it ideal for components that must withstand repeated use and impact.
- 1600 MPa tensile modulus for structural integrity.
- 40 MPa ultimate tensile strength.
- 60 J/m notched impact strength for durability.
Precision Manufacturing Ready
MED413 provides outstanding surface finish quality straight from the printer and excellent machinability for secondary operations. This combination enables high-precision medical components with minimal post-processing requirements.
- Exceptional surface finish quality.
- Superior machinability for precision work.
- Available in clear and white color options.
Technical Specifications
- Cytotoxicity: Passed ISO 10993-5
- Irritation & Skin Sensitization: Passed ISO 10993-10
- Tests for Irritation: Passed ISO 10993-23
- Elongation at Break: 50%
- Tensile Modulus: 1600 MPa
- Ultimate Tensile Strength: 40 MPa
- Impact Strength (Notched): 60 J/m
- Heat Deflection Temperature: 70°C
Please note: ISO and ASTM standard results are valid when using an approved Henkel-validated workflow. Values provided are specific to LOCTITE MED413 CLEAR as a reference; for specific mechanical properties of other colors, please refer to the corresponding documentation.
| Mechanical Properties | Measure Method | Green | Post Processed |
|---|---|---|---|
| Tensile Stress at Break (MPa) | ASTM D638 | 20 - 25 | 35 - 40 |
| Tensile Stress at Yield (MPa) | ASTM D638 | 28 - 23 | 30 - 38 |
| Young’s Modulus (MPa) | ASTM D638 | 850 - 1000 | 1250 - 1400 |
| Elongation at Break (%) | ASTM D638 | 115 - 130 | 105 - 115 |
| IZOD Impact (Notched) (J/m) | ASTM D256 | - | 47 - 52 |
| HDT at 0.455 MPa (°C) | ASTM D648 | - | 38 - 40 |
| HDT at 1.82 MPa (°C) | ASTM D648 | - | 34 - 35 |
| Shore Hardness (3s) (D) | ASTM 2240 | - | 70 |
| Water Absorption (24 hr) (%) | ASTM 570 | - | 0.27 – 0.28 |
Workflow:
Validated workflows need to be followed to achieve properties as provided in the TDS. Examples of validated workflow steps are listed below. Users should defer to the most current workflow information for the best results which can be found here
Printer Settings:
LOCTITE 3D MED413 CL is formulated to print optimally on an industrial DLP printer. Read the safety data sheet carefully to get details about health and safety instructions. Recommended print parameters:
- Shake resin bottle well before usage
- Temperature: 20°C to 25°C
- Intensity: 4 mW/cm² to 8 mW/cm²